4Cr13 is stainless steel material with high hardness and wear resistance. After quenching, it has higher hardness and good corrosion resistance than 3Cr13

Worldwide equivalents of grade: 4Cr13

country / regionChinaEUGermanyJapanUSA
Grade4Cr13X39Cr13 (1.4031)X39Cr13SUS420J2420S45
Chemical Composition of 4Cr13 Steel Material

Mechanical Properties of 4Cr13

HRC hardness: ≥ 50 (Quenched and Tempered)

HBW hardness: ≤ 235 (Annealed)

Physical Properties of 4Cr13

Density (g/cm3): 7.75

Specific heat capacity (J/Kg·K): 460 at 0-100℃

Thermal conductivity (W/m·K):

28.1 at 100℃

28.9 at 500℃

Coefficients of linear thermal expansion (10-6/K):

10.5 (0-100℃)

12.0 (0-500℃)

Electrical Resistivity (μΩ·m): 0.59 at 20℃

Longitudinal modulus of elasticity (kN/mm2): 215 at 20℃

Heat Treatment

750 to 800°C for about 2 to 5 hours
slow controlled cooling of 10 to 20°C per hour to about 650°C;
further cooling in air, max. 200 HB

1000 to 1050°C
15 to 30 minutes keeping curing temperature
quenching in oil/compressed gas/hot bath
obtainable hardness: 53 – 56 HRC

slow heating to tempering temperature immediately after hardening, to 180 to 300 °C depending on desired hardness
1 hour per 20 mm: min. 2 hours

Features and Application




After quenching, the hardness is higher than 3Cr13 and the corrosion resistance is good. The quenching hardness is generally above hrc48.

Industry: it is suitable for electric discharge and grinding. It is suitable for making high-precision injection mold kernel cavity with high mirror surface. It has high hardness and toughness after heat treatment. It can also be used as stamping mold accessories and templates. It is required to clamp fixture molds in contact with the product surface; It is applicable to scenes with high temperature rust prevention and corrosion prevention.

For civil use: it can make tableware knives and outdoor knives.

4Cr13 products

Product typeProductsDimensionProcessesDeliver Status
Plates / SheetsPlates / Sheets0.08-200mm(T)*W*LForging, hot rolling and cold rollingAnnealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Steel BarRound Bar, Flat Bar, Square BarΦ8-1200mm*LForging, hot rolling and cold rolling, CastBlack, Rough Turning, Shot Blasting,
Coil / StripSteel Coil /Steel Strip0.03-16.0x1200mmCold-Rolled & Hot-RolledAnnealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Pipes / TubesSeamless Pipes/Tubes, Welded Pipes/TubesOD:6-219mm x WT:0.5-20.0mmHot extrusion, Cold Drawn, WeldedAnnealed, Solution and Aging, Q+T, ACID-WASHED